1: Winding angle, 45°～65° (winding angle can be adjusted according to different requirements to achieve better mechanical properties);
2: Fiber content (weight ratio), 70% to 75%;
3: Density, 2.00g/cm3;
4: Water absorption, less than 0.03%;
5: Axial thermal expansion coefficient, 1.8E-05 1/K;
6: Glass transition temperature, 110～120℃;
7: Chemical resistance Mineral oil: excellent;
8: Solvent and dilute acid: excellent;
9: Tensile elastic modulus, axial 14000 MPa;
10: Tensile strength: 280 MPa in the axial direction; 600 MPa in the circumferential direction;
11: Shear strength: 150 MPa;
12: Bending strength: axial 350 MPa;
13: Compressive strength: axial 240 MPa;
14: Relative dielectric constant 2-3.2;
15: Dielectric loss factor 0.003-0.015;
16: Partial discharge ≤5;
17: Dielectric strength: axial 3～6kv/mm; radial 10～12kv/mm;
18: Lightning shock: 110KV;
19: Power frequency shock: 50KV;
20: Heat resistance class: B, F, H;
21: inner diameter > 5mm; outer diameter < 300mm; length < 2000mm.
The above data is only for reference, the casing parameters we produce are customized for each customer's needs!
Contact available at :
Jacky Shen - Sales manager
Email：jacky@zjhtxc.com
The filament winding and material parameters of epoxy fiberglass tubes result in a high elastic modulus typically ranging between 2.5-3 GPa (363-435 ksi). This characteristic provides excellent stiffness and stability, making it suitable for use in challenging environments in fields such as chemical engineering, water treatment, marine engineering, etc. Additionally, its outstanding corrosion resistance is also one of the critical reasons why this product is highly favored.